SEO TitlePA66 GF30 Flame-Retardant Glass Fiber Nylon 66 Compound | WanHanMeta Description30% glass fiber PA66 GF30 flame-retardant nylon 66 compound, grade PA66-WHRG30A. TDS values: 125 MPa tensile, HDT 180 C, 0.5% shrinkage. Verify V-0 thickness.
30% Glass Fiber Flame-Retardant PA66 GF30 Nylon Compound
Grade PA66-WHRG30A · Modified nylon 66 with 30% glass fiber and flame-retardant additive · Typical TDS values
URL slug: /pa66-gf30-flame-retardant-glass-fiber-nylon-66-compound
Product Summary
PA66-WHRG30A is a modified PA66 (nylon 66) compound reinforced with 30% glass fiber and a flame-retardant additive system, supplied as pellets for injection molding. It is positioned for preliminary material screening in electrical and electronic housings and in structural injection-molded parts where flame performance must be reviewed. All figures below are typical values taken from the source TDS for the PA66 WHRG30A grade. The TDS states UL 94 V-0 without stating the tested specimen thickness, so buyers should confirm the current grade-specific report, colour and finished-part compliance before approval.
Key Features
- 30% glass fiber reinforcement with 125 MPa tensile strength (ISO 527-2) – stiffness for housings and load-bearing moldings.
- Flexural strength 185 MPa and flexural modulus 6,800 MPa (ISO 178, as cited in TDS) – supports structural part design.
- Heat deflection temperature 180 °C (ISO 75-2/B) – dimensional retention in warm service environments.
- Notched Izod impact 15 kJ/m2 (ISO 179) – impact tolerance for ribs, snap fits and fastening points.
- TDS states UL 94 V-0, specimen thickness not stated – early screening grade; verify thickness-specific report before approval.
- Density 1.52 g/cm3 (ISO 1183) and shrinkage 0.5% (ISO 2577) – part-weight estimation and mold shrinkage planning.
Technical Specifications
| Property | Typical Value | Test Method |
|---|
| Base resin | Modified PA66 (nylon 66) | – |
| Glass fiber content | 30% | Grade designation |
| Flame-retardant system | Flame-retardant additive in modified PA66 | Product data |
| Tensile strength | 125 MPa | ISO 527-2 |
| Flexural strength | 185 MPa | ISO 527-2 (as cited in TDS) |
| Flexural modulus | 6,800 MPa | ISO 178 |
| Notched Izod impact | 15 kJ/m2 | ISO 179 |
| Heat deflection temperature | 180 °C | ISO 75-2/B |
| Density | 1.52 g/cm3 | ISO 1183 |
| Molding shrinkage | 0.5% | ISO 2577 |
| Flammability rating | UL 94 V-0 as stated in TDS (specimen thickness not stated) | UL 94 |
| Source TDS grade | PA66 WHRG30A | – |
Typical values only. Confirm the current grade-specific TDS and compliance documents before design freeze.
Models and Options
PA66-WHRG30A (source TDS grade PA66 WHRG30A) is the flame-retardant GF30 grade described here. WanHan also compounds PA6, PA66, PP, PBT, PC, PC/ABS, ABS, PA11, PA12, PET and PPS formulations for application-specific requirements. Minimum order quantity is 5 kg, and custom-grade lead time is 7–10 days. Monthly PA66 GF30 production capacity is up to 5,000 metric tons, subject to production schedule.
Materials and Structure
The compound combines a modified PA66 base polymer with glass fiber and a flame-retardant additive. Production follows a controlled compounding route: incoming raw-material inspection, controlled feeding, extrusion, water cooling, pelletizing and cutting, multi-instrument laboratory testing, then automatic weighing and packaging. This sequence supports batch-to-batch consistency from sample evaluation through volume production.
Applications
Electrical and electronic housings, plus structural injection-molded parts that require flame-retardant material screening. Final assembly requirements, wall thickness and compliance targets should be validated with the supplied grade documentation before part release.
Customization
Grade selectionFormulation adjustmentGlass-fiber reinforcementHeat stabilizationFlame-retardant modificationToughness modificationColour matchingSample evaluationInjection-molding guidance
TDS files and third-party compliance reports are issued according to the exact grade and application requirements.
FAQ
What is the base resin and glass fiber content of this grade?
Modified PA66 (nylon 66) with 30% glass fiber and a flame-retardant additive system. The source TDS grade is PA66 WHRG30A.
Is UL 94 V-0 confirmed for this material?
The TDS states UL 94 V-0, but the tested specimen thickness is not stated. Confirm the current grade-specific report before product approval.
Which documents are supplied with the material?
TDS documents and third-party compliance testing records are provided according to the exact material grade and application requirements.
What are the minimum order quantity and lead time?
MOQ is 5 kg, and custom-grade lead time is 7–10 days.
What monthly capacity is available for PA66 GF30?
Up to 5,000 metric tons per month, subject to production schedule.
Can the formulation or colour be customized?
Yes. Support includes grade selection, formulation adjustment, glass-fiber reinforcement, heat stabilization, flame-retardant modification, toughness modification, colour matching and injection-molding processing guidance.
Which quality systems are in place?
ISO 9001:2015, ISO 14001:2015 and ISO 45001:2018 management systems, covering the design and production of modified plastic pellets.
Image Filename and Alt Suggestions
Suggested filename: pa66-whrg30a-gf30-flame-retardant-nylon-compound.png
Alt text: PA66 GF30 FR(V0) material sample for flame-retardant nylon compound screening.
Inquiry Information
Guangdong Wanhan New Material Technology Co., Ltd. (WanHan Plastic)
Email: gdwanhan@163.com · Tel / WhatsApp: +86 135-3701-2277
Website: www.wanhan-plastic.com
Address: No. 3 Xingqi East Road, Dongxing District, Dongjiang Science and Technology Park, Zhongkai High-tech Zone, Huizhou City, Guangdong Province, China
Send your part design, wall thickness and compliance target to receive grade selection, sample arrangement and TDS documentation.