Meta Description: Modified PA6 with 30% carbon fiber, black. Tensile 161 MPa, flexural modulus 10930 MPa, HDT 213 °C at 1.8 MPa. Request TDS and current batch documentation.
H1: Carbon Fiber Reinforced PA6 Compound With 213 °C HDT and UL 94 HB
Product Summary
PA6-WHC30BK is a black modified nylon 6 (PA6) compound reinforced with 30% carbon fiber, supplied as pellets for injection molding. It is aimed at structural injection-molded components and mechanical housings and fixtures where stiffness and dimensional control matter. The published datasheet lists a tensile strength of 161 MPa, a flexural modulus of 10930 MPa and a heat deflection temperature of 213 °C at 1.8 MPa. Values are typical and should be checked against current batch documentation before part approval.
Key Features
30% carbon fiber reinforcement
Tensile strength 161 MPa and flexural modulus 10930 MPa support stiff, load-bearing molded parts.
213 °C heat deflection temperature
HDT at 1.8 MPa gives engineers a documented thermal baseline for elevated-temperature service.
Flow shrinkage 0.3–0.4%
A narrow shrinkage window at 3.18 mm helps with dimensional control and tooling planning.
Notched Izod 13.7 kJ/m²
An impact figure measured at 3.2 mm (ISO 180-1A) that can feed directly into design review.
Density 1.29 g/cm³
Lets engineers estimate part mass early in material selection instead of after tooling.
UL 94 HB listed
A documented flammability classification for preliminary compliance screening.
Technical Specifications
Property
Value
Grade / model
PA6-WHC30BK
Base polymer
Modified PA6 (nylon 6)
Reinforcement
Carbon fiber 30%
Color
Black
Density
1.29 g/cm³ (ISO 1183)
Tensile strength
161 MPa (ISO 527-2/50)
Flexural modulus
10930 MPa (ISO 178)
Flexural strength
203 MPa (ISO 178)
Notched Izod impact
13.7 kJ/m² at 3.2 mm (ISO 180-1A)
Heat deflection temperature
213 °C at 1.8 MPa (ISO 75-2/A)
Flow shrinkage
0.3–0.4% at 3.18 mm (ISO 294-4)
Flammability
UL 94 HB
Typical values only. Confirm current batch documentation before design approval.
Models and Options
The documented grade is PA6-WHC30BK, referenced in the datasheet note as PA6 WH-CF30BK: a black modified PA6 with 30% carbon fiber. No further PA6 carbon-fiber grades are documented in the material provided here. Where a project needs a different balance of stiffness, heat resistance or flame performance, that becomes a development request rather than a catalogue choice, and must be confirmed against the actual part requirements.
Materials and Structure
A modified PA6 matrix compounded with carbon fiber and supplied as black pellets. Grade identity is verified by the bag label and the TDS; photographs of pellets are a visual reference only and cannot confirm fiber content.
Structural injection-molded components, mechanical housings and fixtures. Suitability requires part-level validation against the real load case, service temperature and chemical exposure of the finished part.
Customization
WanHan supports material selection, custom formulation development, glass-fiber reinforcement, heat stabilization, flame-retardant modification, toughness modification, color matching, sample evaluation and injection-molding processing guidance. Any change to this grade is handled as a development project and confirmed against the customer's part design and service conditions.
FAQ
Are the datasheet values guaranteed for every batch?
The values are typical values only. Request the PA6 WH-CF30BK TDS for preliminary material screening and confirm current batch documentation before approval.
What heat deflection temperature does this grade reach?
213 °C at 1.8 MPa (ISO 75-2/A), a typical value for PA6-WHC30BK.
Does this grade carry a UL 94 V-0 rating?
No V-0 rating is stated. The documented classification is UL 94 HB. If V-0 is required, discuss a flame-retardant formulation as a development request.
How much does the carbon fiber reduce shrinkage?
Flow shrinkage is listed at 0.3–0.4% at 3.18 mm (ISO 294-4). Shrinkage differs by direction, so validate tooling with part-level trials.
What are the MOQ and lead time?
MOQ and lead time for PA6-WHC30BK are not published in the material provided. Contact WanHan to confirm quantities for sample evaluation and volume production.
Is the color customizable?
PA6-WHC30BK is documented in black. Color matching is listed among WanHan's compounding services, so an alternative color can be reviewed as a development request.
Can the pellets be identified from a photograph?
No. Fiber content and grade identity are confirmed by the bag label and the TDS, not by a photo of the pellets.
Inquiry Information
Guangdong Wanhan New Material Technology Co., Ltd. (WanHan Plastic)
Email: gdwanhan@163.com
Tel / WhatsApp: +86 135-3701-2277
Address: No. 3 Xingqi East Road, Dongxing District, Dongjiang Science and Technology Park, Zhongkai High-tech Zone, Huizhou City, Guangdong Province, China
Send your part drawing, required temperature range and target quantity to start material screening.
Image Filename and Alt Suggestions
pa6-whc30bk-carbon-fiber-pellets-poured-view.png — Alt: Poured view of black 30% carbon fiber reinforced PA6 compound pellets
pa6-whc30bk-carbon-fiber-pellets-top-view.png — Alt: Top view of black CF30 PA6 compound pellets in a container
pa6-whc30bk-carbon-fiber-pellets-white-background.png — Alt: Black modified PA6 compound pellets with carbon fiber on a white background