| Type | Carbon-fiber-reinforced PA6, black | Model | PA6-WHC30BK |
| Params | Carbon fiber 30% (grade designation). Density 1.29 g/cm3 (ISO 1183). Tensile strength 161 MPa (ISO 527-2/50). Flexural modulus 10930 MPa; flexural strength 203 MPa (ISO 178). Notched Izod 13.7 kJ/m2 at 3.2 mm (ISO 180-1A). HDT 213 C at 1.8 MPa (ISO 75-2/A). Flow shrinkage 0.3-0.4% at 3.18 mm (ISO 294-4). UL 94 HB. Typical values only. | Material | Modified PA6 with carbon fiber, black |
| Applicable Industry | Structural injection-molded components, mechanical housings and fixtures; suitability requires part-level validation. | ||
Carbon-fiber reinforcement for stiffness and dimensional control. Use the PA6 WH-CF30BK TDS for preliminary material screening; request current batch documentation and validate processing and finished-part performance before approval.

Representative CF-reinforced compound pellets, poured view. Visual reference only; grade identity is verified by label and TDS.

Representative CF-reinforced compound pellets, top view. Visual reference only; fiber content cannot be confirmed from a photo.

Representative CF-reinforced compound pellets, white-background view. Visual reference only; not a grade-specific test record.